WICKS MISSION STATEMENT
  At Wicks we are committed to
  providing exceptional, fast and
  friendly service. By supplying
  and supporting a broad range
  of products and materials,our
  mission is to help you complete
  your next project on schedule
  and with quality parts and
  materials.
Registered UsersSign In
View Cart View RFQs Express Ordering  | Shipping 
 | Tax 
 | Terms
 Shopping Cart 0 Items
 Request for Quote 0 Items
All Categories > Composites & Finishing Materials > Vacuum Bagging  
 

Vacuum Bagging


Click on a Product to view details.

Bagging Film WL7400

Bagging Film WL7400


Nylon vacuum film is .002" thick, 48" wide: v-fold. Elongation at break 350+, tensile strength - 8000 psi, maximum temperature use - 390°F, Melt point minimum 414 degree F, Yield: 24,500 inch x2/#/mil. Color- green/blue, shelf life - 18 months.
Price is per yard.
Bagging Film D250

Bagging Film D250


Room temperature to 200 degree F, this film is very dependable and releases easily from the sealant, so expect to use the same piece of film for all the compaction cycles. Color: blue, tensile strength: 4000 psi, tear resistance: 400 ply, ultimate elongation: 430%, width: 55 inches.
Price is per yard.
Release Ply

Release Ply


Release Ply B is a heat set and scoured smooth weave nylon fabric used as a release fabric directly against bond lines or laminated where a finish for subsequent bonding or painting is needed. Excellent for controlling adhesive squeeze out, release B, may stick on 350 degree F cures, and works well on all fiberglass/epoxy laminates. 60" width, white nylon weight: 2 oz., Grab tensile: warp - 110 lbs. filling - 140 lbs (min).
Price is per yard.
Peel Ply

Peel Ply


1.8 oz woven polyester cloth 63" wide. Sold by the running yard only. Ideal for usage as peel ply. Price is per yard.
Price is per yard.
Release Film D7000

Release Film D7000


Exhibits superior release qualities over the entire temperature range. The elongation allows for superior conformability for irregular shapes. Elongations: 550%, maximum temperatures 600 degrees F, thickness: .001, width: 48", color: red.
Price is per yard.
Release Film W4600B

Release Film W4600B


Blue, 54# wide, .002 thick release material. Elongation - 300%, maximum temperature use: 400 degree F. Shrinkage 2.5% at 400 degree F. Releases without contamination from phenolics, epoxies and polyesters. 18 mo shelf life.
Price is per yard.
Breather-Bleeder

Breather-Bleeder


4 oz. 60" wide, 1/8" thick polyester breather material that stretches to all contours. One layer will conduct air at 50 psi. N4 is not a release material and should be used with release film - #4600. Maximum use temperature - 400 degree F.
Price is per yard.
Release Fabric Ply BLB1

Release Fabric Ply BLB1


Ply B peel ply coated with a release agent that releases all aircraft resins up to 400 degrees F. Use with R300 sensitive tape as all coated peel plies have the potential to transfer. 60" wide, 2 oz. nylon peel ply is .004 - .005 thickness. Grab tensile: warp - 110 LBS. filling - 140 LBS. minimum.
Price is per yard.
Vacuum Valve

Vacuum Valve


2 piece cast aluminum valve makes vacuum bag connections positive and fast. Simply insert through bag by cutting an X in the film, the round bottom base plate is designed to keep breather from compressing under the plate and sealing off. Successfully tested to hold 29 inches of mercury and 200 psi at temperatures up to 500 degrees F.
Venturi Generator

Venturi Generator


Works with any air compressor delivering at least 65 psi at 3.5 SCFM. (Operating range 40-100 psi) Develops over 20 inches Hg of vacuum (10 psi) & will evacuate 2.2 SCFM at 0 inches Hg.
Quick Disconnect Tool

Quick Disconnect Tool


AQD500TF high temperature disconnects are two way shut off fittings. When disconnected, air flow is shut off in both the plug and socket allowing your vac valve to remain under vacuum pressure after being disconnected. Parts can be moved without losing vacuum. The socket or coupler is equipped with a threaded female fitting that creates an air tight seal when inserted into airflow. The plug portion has a female 1/4" standard pipe thread. The sleeve portion of the coupler portion retracts upward, away from opening the receives the plug half. This sleeve is spring loaded so when released it returns to original position. Sleeve must be retracted before coupling is achieved and must return to original position to create an airtight seal ...
Vacuum Gauge 885-5

Vacuum Gauge 885-5


Necessary in monitoring the vacuum level/clamping force during the cure time of the laminate. 2 inch diameter gauge has 1/4" NPT fitting and reads 0 to 30 pounds per square inch. 0 to 100 KPA VAC/KPA.
Vacuum Gauge VG-30

Vacuum Gauge VG-30


Durable vacuum gauge determines how much vacuum pressure is under your vacuum bag. Gauge is calibrated in both inches of mercury ad metric units and has a rubber jacket to protect it from damage. The stem is 1/4" pipe thread that can be used with the AQD500 quick disconnect. To get a reading place the gauge in the diagonal corner from your vacuum port. After pulling full vacuum, disconnect vacuum source. Allow a little air to reenter through port and within seconds the gauge should register a drop in pressure. Reads 0 to 30 lbs. per sq. inch. 0 to 100 KPA
Sealant Tape

Sealant Tape


Multipurpose sealant tape that can be used for cures to 375° F. Seals easily to metal or composite tooling. Tape is yellow, 1/8" thick by 1/2" wide, 25 ft roll.
Partall Parting Agent

Partall Parting Agent


Wax based compound useful as a general purpose parting agent on metal molds as well as a prime coat for part all mold release. A thin coat evenly applied to a mold is usually good for 3-5 cycles. Simply apply the paste to the mold surface, allow to dry, then buff.
Partall Mold Release

Partall Mold Release

(2)
For brushing or spraying on molds to prevent resin from sticking to the mold. A green viscous water/alcohol film-forming solution, water soluble, particularly recommended as a parting layer or separator between polyester or epoxy resin and mold surfaces of most kinds. Not recommended for use with resins containing water or giving off water during the cure-phenolics for instance. #10 part all is generally applied at room temperature to form a smooth, very glossy film. Will not shrink and pull away from corners or curved surfaces. After resin is cured the film will part easily from the mold and is readily dissolved from the molded parts with water. Use after tool has been paste waxed with part all paste. QT - ORM-D. 5-gal - Hazard - Ship ...
Image

Bagging Film D316


D316 is a green-tinted, transparent, heat-stabilized, co-extruded film produced from a modified nylon 6 resin which can be used for cures up to 400 degrees F.

D316 is recommended as bagging film for advanced composite fabrication and other high temperature pressure applications where softness, workability and defect-free films are essential.

Tensile strength 12000 psi, tearing strength 90 gm/mil, elongation over 300%, width 55 inches. Price is per yard.